Non-subliming Mid-UV dyes and ultra-thin organic arcs having differential solubility

ABSTRACT

Mid-UV dyes enabling ultra thin antireflection coatings for multi-layer i-line photoetching are produced from bichalcones; bis-a-cyanoacrylates/bis-cyanoacrylamides; and 1.4 divinylbenzenes. The dyes are nonsubliminal and differentially insoluble in standard photoresist solvents.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention generally relates to Anti-Reflective Coatings (ARCs) for multi-layer i-line photoresist systems. More particularly, it relates to improved i-line dyes, which dyes have differential solubility characteristics for use in ultra-thin layer ARCs.

2. Background of the Prior Art

Recently, integrated circuit (IC) manufacturers when printing submicron feature sizes in the range of 0.35-0.70 microns have relied upon mid-ultraviolet (mid-UV) sensitive photoresist. The principal exposure wavelength for these photoresists is 365 nm, which corresponds to the i-line spectral peak of the Hg-Xe arc lamp. The use of this shorter wavelength, as compared to the 436 nm g-line peak, permits greater resolution and broadens depth of focus. Thus, the term "i-line resist" has been used inter-changeably with "mid-uv photoresist". The resolution of i-line resists can be further enhanced by providing substrate reflection control. This can be achieved in two ways. The first way is by adding dye into the resist at some expense to photospeed and feature profile quality. The second way is by employing a multi-layer resist scheme wherein a dyed bottom layer plays the light absorbing role.

Two types of multi-layer schemes have been used in the industry. At one time, relatively thick (ca. 1 micron) bottom layers having low dye concentration were popular. It is desirable that those bottom layers now be replaced by high optical density, ultra-thin ARCs to simplify the etching of the ARC, which would lead to improved critical dimension control. However, the development of ultra-thin ARCs for i-line applications has been hampered by the unavailability of suitable dyes.

Some advances have been made in developing prior art i-line dyes for single-layer-resist-type processes. However, there is a drawback to such dyes, as well as dyes designed for the multi-drawback resist processes, which accomodate a relatively thick (1.3 micron) bottom or sublayer ARC. This drawback of the prior art and their attendant i-line dyes are explained below.

An example of a classically cited strongly absorbant mid-UV i-line dye in the prior art is Michler's ketone (bis-N,N-dimethylaminobenzophenone). In order to employ Michler's Ketone in photo-etch processing, conditions peculiar to such processing must be accommodated. That is, it is common to process photoresist layers and their ARCs at temperatures as high as 200° C. Unfortunately, Michler's Ketone, like many other prospective i-line dyes, tends to sublime or volatize at such temperatures, and therefore lacks the requisite thermal stability to undergo such processing.

In U.S. Pat. No. 4,719,166, R. W. Blevins disclosed a single layer non-subliming resist system which used butadienyls as i-line dyes. The dyes surprisingly overcame the tendency of previously known mid-UV dyes to sublime at processing temperatures near 200° C., even though the molecular weight of the butadienyls was less than the molecular weight which would have predicted thermal stability. The predictably higher molecular weight dyes, as taught by Blevins, were to be avoided because they would not exhibit good solubility in photoresist solvents such as chlorobenzene and ethoxyethyl acetate. A drawback of these dyes is that the process used to produce the butadienyls yields the butadienyls at an unacceptably low 10%. More importantly, these dyes are so soluble that they cannot be used in ultra-thin ARCs without leaching into the photoresist top layer of multi-layer systems.

In U.S. Pat. No. 5,139,918, Mr. A. Goel disclosed a multi-layer resist system which employed butadiene or bromine substituted butadienes as the i-line dye, especially N,N'-dibutyl-N,N'-di(1-(4,4-dicyano-1,3-butadiene))-1,6-hexanediamine. Although this dye system is acceptable for the relatively thick (1.3 micron) bottom layers of the multi-layer resist systems, it is ineffective for ultra-thin ARCs. Like the single layer i-line dyes, these butadienes are highly soluble in photoresist solvent systems. Therefore, although the 1.3 micron thickness of the bottom layer ARC serves to lessen the leaching, ultra-thin ARCs suffer so much loss of dye that substrate reflection cannot be controlled.

The drawback to each of these prior art i-line dyes is that they lack effective differential solubility. That is, the very same solubility in photoresist solvents such as chlorobenzene and ethyoxyethyl acetate which allow the dyes to be formulated in known polymer coating systems such as polymethyl methacrylate (PMMA), will either limit dye use to single layer photoresist systems, or risk, in multi-layer systems, having the dye leaching out of the ARC layer into the top photoresist layer.

Accordingly, a non-subliming i-line dye having strong mid-UV absorptivity which would be sufficiently soluble in ultra-thin ARC layers to produce an effective high optical density in layers having less that 0.25 microns thicknesses, yet characterized by being insoluble in photoresist solvents, would represent an unexpected advancement in the art and fulfill a long felt need in the industry.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide an i-line dye system with sufficiently selective differential solubility to avoid leaching out of ultra-thin ARCs.

It is a further object of the present invention to provide a non-subliming i-line dye at 200° C. which would be soluble in ARC solvent but not photoresist solvent.

It is a still further object to provide a non-subliming i-line dye which can be produced in commercially acceptable yields.

Applicant has developed mid-UV dyes which enable ultra-thin ARCs for multi-layer i-line photoetching where the ARC can be sandwiched between a top layer i-line photoresist and substrate without risk of the dye leaching into the photoresist. The dye is termed differentially insoluble in standard photoresist solvents.

Dyes of the present invention can be generally described as dienyl compounds having molecular weights greater than 300 g/mol and which are soluble in NMP but not chlorobenzene or 2-ethoxyethyl acetate. These dyes may be described as fitting in one of the following three chemical families of structures:

1. bischalcones

2. bis-a-cyanoacrylates (and bis-a-cyanoacrylamides)

3. 1,4-divinylbenzenes

The i-line dyes of the present invention can all be prepared in high yield from low cost, commercially available starting materials.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

In accordance with the present invention, a first preferred family of i-line dyes having the requisite differential solubility and non-subliming characteristics comprise symmetrical structures having two identical chalcone moieties linked by appropriate spacer groups (R₂). The bischalcone compounds may be represented by the following general formula: ##STR1## where R₁ is chosen from the group: ##STR2## where R₂ is selected from the group: --O--CH₂ --CH₂ --O--CO--R₄ --CO--O--CH₂ --CH₂ --O--; --NH--CO--R₄ --CO--NH--;

--O--R₅ --O--; --CH₂ --; --O--; --S--;

where R₃ =--H, --CH₃, halogen, --OH, or --OCH₃ ; where R₄ is chosen from the group: ##STR3## where R₅ is an aliphatic, cycloaliphatic, or alkylaryl divalent radical such as: ##STR4##

A particularly preferred representative dye of this family is as follows: ##STR5##

In accordance with the present invention, a second family of preferred i-line dyes having the requisite differential solubility and non-subliming characteristics are bis-a-cyanoacrylates and bis-a-cyanoacrylamides having the general formula: ##STR6## where R₁ is defined as above and where R₆ is selected from the group: ##STR7## and where R₄ and R₅ are defined as above.

A particularly preferred representative dye of this family is as follows: ##STR8##

Likewise, in accordance with the present invention, a third family of preferred i-line dyes having the requisite differential solubility and non-subliming characteristics are the 1,4-divinylbenzenes having the general formula: ##STR9## where R₇ is selected from the group: ##STR10## where R₈ is an alkyl, cycloalkyl, or alkylaryl monovalent radical such as methyl, ethyl, cyclohexyl, or benzyl; where R₉, R₁₀ and/or R₁₁ are --H, --CH₃, --OH, --OCH₃, halogen, or --O--CH₂ --CH₂ --OH; and where A! is a monovalent anion such as chloride, bromide, tosylate or methanesulfonate.

A particularly preferred representative dye of this family is as follows: ##STR11##

The characteristics of the dye compounds of the present invention are:

1. exhibiting low solubility (<2 wt. %) in commonly used photoresist solvents such as ethylene (propylene) glycol monomethyl ether acetate (EGMEA and PGMEA), chlorobenzene, butyl acetate, 3-ethoxyethyl propionate, and ethyl lactate;

2. exhibiting solubility to >1.5 wt. % in preferred solvent systems for ultra-thin bottom anti-reflective coatings, e.g., N-methylpyrrolidone, g-butyrolactone, tetrahydrofurfuryl alcohol, and mixtures thereof with higher volatility cosolvents such as cyclohexanone, diglyme, and diacetone alcohol;

3. possessing a molar extinction coefficient (expressed in L/mol-cm) in excess of 10,000 and, more preferably, in excess of 20,000 at i-line;

4. remaining effectively non-subliming over the temperature range 100°-220° C. when the dye is present in an ultra-thin anti-reflective coating applied onto a semiconductor substrate and when said coating is baked on a hot plate within the stated temperature range for 10-120 seconds.

These compounds unexpectedly enable i-line ARCs having ultra-thin thicknesses of less than 0.25 microns, preferably 0.05 to 0.20 microns. The ARCs comprise a solvent (or solvent mixture), an organic polymer binder and the i-line dye(s). The dyes will be present in an amount of 25 wt. % to 60 wt. % thus providing high film absorbance at i-line ranging typically from 0.3/1000 Å to 0.9/1000 Å. Despite the ultra-thin characteristics and heavy dye loading of the ARC, there is no microscopic intermixing (defined as less than a 0.01 micron zone centered at the photoresist/ARC interface) with i-line photoresists such as OIR® 32 (OCG Corporation trademark) either when applied or baked.

Preferred polymer binders for ultra-thin ARCs incorporating the new dyes are copolymers with high glass transition temperatures such as polyamic acids, polyarylethers, polyarylsulfones, aromatic polyamides, solvent-soluble polyimides, and aromatic polyureas. Examples of especially useful binders include the following polymers:

1. polyamic acid prepared by the reaction of 4,4'-oxydianiline and pyromellitic dianhydride;

2. polyamide prepared from dimethyl terephthalate and 2,2,4-trimethylhexanediamine (known commercially as Trogamid®, Huls America trademark);

3. polysulfone prepared as the reaction product of 4,4'isopropylidenediphenol and 4,4'-chlorophenylsulfone (known commercially as Udel®, Amoco Performance Products trademark);

4. polyurea prepared as the reaction product of bis(4- 4-amino-phenoxyl!phenyl)sulfone and methylene-di-p-phenyl diisocyanate.

ARCs incorporating the new dyes are prepared by dissolving the polymer binder and the dye(s) in the preferred ARC solvents described above to a total solids concentration of 3 wt. % to 10 wt. %. The total solids concentration is adjusted so that when the coating is spin coated at 2000-6000 rpm for 30-90 seconds on a semiconductor substrate and then hot plate baked at 100°-220° C. for 30-120 seconds, the desired coating thickness will be obtained in the range of 0.05 microns to 0.25 microns. Spin coating at 2500-5000 rpm for 60-90 seconds is preferred to obtain defect-free coatings. Likewise, baking at 150°-210° C. for 30-60 seconds is preferred to achieve the best lithographic performance with most resists. (Defect-free refers to the absence of thickness variations, voids, pinholes, dewetted areas or particulate matter.) Organosilanes such as 3-aminopropyltriethoxysilane and/or surfactants such as Fluorad® FC-430 (3M Corporation trademark) may be added to the ultra-thin ARCS at levels of 0.01 wt. % to 0.5 wt. % to improve the adhesion and wetting character-istics of the coatings.

The following examples further illustrate the invention.

EXAMPLE 1 Preparation of Bis-A-Cyanoacrylamide Dye from Diamine, Ethyl Cyanoacetate, and Vanillin ##STR12## Procedure

To a 5 L, four-necked, round-bottomed flask equipped with a mechanical stirrer, thermometer, reflux condenser, and temperature probe with rheostat controller and heating mantle was added 197.56 g (1.70 mmol) of 2-methyl-1,5-pentanediamine. To this diamine was slowly added with stirring, 384.60 g (3.40 mmol) of ethyl cyanoacetate. The reaction of 2-methyl-1,5-pentanediamine and ethyl cyanoacetate produced an initial exotherm. When the exotherm subsided, the solution was heated at reflux for 1 h to give a clear, dark orange solution. Heating was temporarily removed and the solution diluted with 1200 ml of ethanol. To the diluted solution was added 517.32 g (3.40 mmol) of vanillin and 12.00 g (100.70 mmol) of N-methyldiethanolamine as a catalyst, followed by an additional 1200 ml of ethanol. Heating was reapplied and the dark orange solution maintained at reflux for 3.5 h. The solution was slightly cooled and 12.00 g (122.34 mmol) of concentrated sulfuric acid was added to neutralize the reaction mixture. The solution was stirred overnight at room temperature to allow the dye to crystallize from the solution.

The crystallized dye was collected by vacuum filtration using 500 ml of isopropanol for rinsing and washing. The collected dye was allowed to dry in the filtration funnel for 20 minutes and then washed twice with 1000 ml portions of deionized water to remove salts. Subsequently, it was washed with three 1000 mL portions of acetone to remove unreacted starting materials and soluble by products. The wet solid was placed in a glass baking dish and air dried for two days to give 620.20 g (70.6% yield) of light orange colored dye. The dye exhibited a molar extinction coefficient of 38,700 L/mol-cm in tetrahydrofurfuryl alcohol.

EXAMPLE 2 Preparation of Bischalcone Dye from Hydroxyacetophenone and Terephthaldehyde ##STR13## Procedure

A 500 ml round-bottomed flask equipped with magnetic stirring bar and condensor was charged with 100 ml of ethanol, 12.40 (74.6 mmol) of acetovanillone and 5.00 g (37.3 mmol) of terephthaldehyde. The stirred mixture was first warmed to give a solution and the solution then cooled to 15° C. To the stirred solution at 15° C. was added 66.0 g (181 mmol) of tetramethylammonium hydroxide (25 weight % aqueous solution) over 18 min, with the temperature rising to a maximum of 25° C. The reaction flask was covered with aluminum foil to protect light sensitive chalcone and stirring continued at ambient for 2 days.

The resulting reaction product was added dropwise to 450 g of stirred 1.5N HCl. Solid terephthalaldehyde-derived chalcone was collected by filtration and washed on the filter with three 200 ml aliquots of deionized water, two 100 ml aliquots of ethanol, and two 25 ml portions of acetone. Drying gave 13.8 g (86% yield) of yellow bischalcone that exhibited a molar extinction coefficient in N-methypyrrolidone (NMP) of 42,112 L/mol-cm. About 13.4 g of the product was stirred with 150 ml of boiling ethanol for 0.5 h, the mixture filtered hot, the precipitate washed on the filter with 50 ml of acetone, and then dried to give 8.2 g (52% yield, overall). The melting point of the purified yellow diphenolic chalcone was 234°-239° C. and the extinction coefficient in NMP was 49,550 L/mol-cm.

EXAMPLE 3 Preparation of Bischalcone Dye from Alkoxyacetophenone and Terephthaldehyde ##STR14## Procedure

A 250 ml round-bottomed flask equipped with magnetic stirring bar and condensor was charged wtih 82 ml of ethanol, 9.01 g (60.0 mmol) of 4-methoxyacetophenone, and 4.02 g (30.0 mmol) of terephthalaldehyde. The stirred mixture was heated gently to give a solution. To this stirrred solution at 23° C. was added 28.1 g (77.0 mmol) of 25 weight % tetramethylammonium hydroxide over 16 min. During the hydroxide addition, a precipitate almost immediately formed. The base addition was interrupted, an additional 80 ml of ethanol added, the chalcone lump broken up, and the rest of the tetramethylammonium hydroxide added. The final reaction mixture temperature was 26° C. The reaction mixture was then protected with aluminum foil and stirred at ambient for 3 days. The mixture was placed in the freezer for several hours; and with the mixture temperature being 0° C., the product was collected by filtration. The bischalcone was washed on the filter with ethanol followed by three 300 ml portions of deionized water. After drying, the yield of crude cream-colored solid was 10.63 g (89%), mp 221°-246° C. The molar extinction coefficient in NMP was 44,700 L/mol-cm at 365 nm.

EXAMPLES 4-27

The data for other representative dye structures from Families 1-3 are summarized in Table I.

See Table I, Dye Examples 4-27

                                      TABLE I                                      __________________________________________________________________________     DYE EXAMPLES 4-27                                                              __________________________________________________________________________     FAMILIES 1 & 2                               Formula Weight                                                                         Extinction                                                                     Coefficient               Example Aldehyde     Spacer Group       Family                                                                              (g/mole)                                                                               (L/mole-cm ×                                                             10.sup.-4)                __________________________________________________________________________      4      cinnamaldehyde                                                                              4,4'-diacetylphenyl ether                                                                         1    482     5.69                       5      N,N-dimethylamino-                                                                          2-methyl-1,5-pentanediamine/ECA*                                                                  2    513     3.65                              benzaldehyde                                                            6      furylcrolein 1,3-propanediamine/ECA                                                                            2    416     5.83                       7      hydroxybenzaldehyde                                                                         2-methyl-1,5-pentanediamine/ECA                                                                   2    459     2.18                       8      3,4-dimethoxybenzaldehyde                                                                   2,2,4-trimethylhexanediamine/ECA                                                                  2    589     4.73                       9      3,4-dimethoxybenzaldehyde                                                                   amine-terminated urethane oligomer/ECA                                                            2    802     4.79                      10      cinnamaldehyde                                                                              di(2-hydroxyethyl)ester of PMDA**/ECA                                                             2    707     5.55                      11      vanillin     1,2-propanediamine/ECA                                                                            2    477     3.81                      12      3,4-dimethoxybenzaldehyde                                                                   2-methyl-1,5-pentanediamine/ECA                                                                   2    547     4.68                      __________________________________________________________________________     FAMILY 3                                                                               Reactant with Terephthaldicarboxaldehyde                                                             Yield (%)                                                                               MP(°C.)                          __________________________________________________________________________     13      4-hydroxyacetophenone 82       --    370     3.32                      14      acetophenone          --       --    338     3.83                      15      N-2-hydroxyethyl cyanoacetamide                                                                      77       237   354     2.65                      16      4-hydroxy-2-methylacetophenone                                                                       60       250-255                                                                              398     3.18                      17      4-hydroxy-3-methylacetophenone                                                                       --       --    398     4.80                      18      3,4-dimethoxyacetophenone                                                                            80       200-216                                                                              458     5.34                      19      2-hydroxy-6-methoxyacetophenone                                                                      70       199-205                                                                              430     4.09                      20      4-hydroxy-3,5-dimethoxyacetophenone                                                                  54       245-250                                                                              490     4.27                      21      2-hydroxy-4-methoxyacetophenone                                                                      46       230-243                                                                              430     3.49                      22      2-hydr5oxy-5-methoxyacetophenone                                                                     58       152-210                                                                              430     1.68                      23      2-hydroxyacetophenone 65       223-245                                                                              370     1.99                      24      3-hydroxyacetophenone 98       210-213                                                                              370     1.41                      25      2,4-dihydroxyacetophenone                                                                            88       --    402     1.39                      26      4-hydroxy-2-methylacetophenone                                                                       60       250-255                                                                              398     3.18                      27      4-hydroxyethoxyacetophenone                                                                          85       249-255                                                                              458     3.71                      __________________________________________________________________________       */ECA denotes reaction product of diamine with two moles of ethyl             cyanoacetate; **PMDA is pyromellitic dianhydride.                        

EXAMPLE 28 Using a Dichalcone Dye in a Polyamic Acid-Based ARC

The dichalcone dye described in Example 2 was dissolved in a polyamic acid solution formulated with solvents NMP and cyclohexanone to achieve a weight ratio of dye to other ingredients (excluding solvents) of 0.67:1.00. This ARC formulation was spincoated onto three separate glass slides at 5000 rpm for 60 seconds. The three slides were baked on a hot plate at respective temperatures of 168°, 200°, and 230° C. for 60 seconds. For adjusted film thicknesses of 1300 Å, the absorbances at I-line were 0.61, 0.60, and 0.59, indicating that dye sublimation was not occurring as bake temperature increased.

To demonstrate the lithographic capability of the ARC, the formulation was spin coated at 5000 rpm for 60 seconds onto a silicon wafer that had been treated with Brewer Science's APX adhesion promoter and the coating was then baked on a hot plate at 168° C. for 60 seconds. A positive-working photoresist (Shipley Microposit® 1470) soluble in propylene glycol methyl ether acetate (PGMEA) was immediately applied over the ARC by spin coating at 5000 rpm for 30 seconds. The resist was soft baked for 30 seconds

on a hot plate at 100° C. and exposed on a stepper with a mercury-xenon light source. The specimen was then developed in aqueous tetramethylammonium hydroxide (Shipley MF®-319 developer) for 45 seconds at ambient temperature to clear the exposed areas of the resist and those portions of the ARC immediately beneath the exposed resist. Microscopic examination showed that the cleared areas were residue-free and that stable 0.7 μm features were resolved.

EXAMPLE 29 Using a Bis-A-Cyanoacrylamide Dye in a Polyurea-Based ARC

An ARC formulation was prepared by combining 144.40 g of 20% solids polyurea solution in tetrahydrofurfuryl alcohol (THFA), 23.10 g of the bis-a-cyanoacrylamide dye from Example 1, 568.58 g of cyclohexanone, and 379.06 g of THFA. (The polysulfone was a copolymer of bis(4- 4-aminophenoxy!phenyl)sulfone and methylene-di-p-phenyl diisocyanate.) The solution was ion exchanged with 50 g of Rohm and Haas Amberlite® 200C(H) ion exchange beads for 4 h to remove ionic contaminants. A sample was then taken and the thickness checked to give 1300 Å±50 Å. The ion exchange beads were removed with a coarse screen and the final formulation filtered through a 0.2 μm capsule filter.

The experimental ARC was spin coated for 60 seconds at 2500 rpm onto a 6" silicon wafer and baked on a hot plate for 60 seconds at 200° C. to obtain a defect-free film with a thickness of 1332 Å (by ellipsometry). An ethyl lactate-based, i-line photoresist capable of submicron resolution (IX 500 EL from Japan Synthetic Rubber) was spin coated over the ARC and soft baked at 100° C. for 90 seconds in proximity. The resist was exposed with a Nikon I-line stepper (0.50 numerical aperature) for 580 msec and then post-exposure baked at 110° C. for 90 seconds in proximity. The wafer specimen was then single-puddle developed for 40 seconds in aqueous tetramethylammonium hydroxide to generate the line & space patterns shown in FIG. 1. (The unetched ARC film can be seen beneath and between the resist features.) The high quality of the resist features, i.e., the presence of highly vertical resist feature sidewalls and the absence of any rounding at the bottom of the resist features, as well as the linearity of the pattern critical dimension (CD) and mask CD (FIG. 2) was evidence of the excellent compatibility of the ARC and photoresist.

EXAMPLE 30

Using a sublimable, photoresist-soluble dye in a polyimide-based ARC. Comparison with performance of ARC from Example 28.

Dicinnamalacetone (DCA, structure shown below) was selected as an example of a highly absorbing I-line dye which is sublimable at ARC processing temperatures and is soluble in photoresist solvents such as propylene glycol methyl ether acetate (PGMEA). ARCs were prepared from DCA and evaluated to demonstrate 1) the negative relationship between bake temperature and film absorbance and 2) the excessive removal of DCA from the film during photoresist application. ##STR15##

Dicinnamalacetone Formula Weight=286.38 g/mol MP=145° C.

Dicinnamalacetone was combined with polyamic acid solution (in NMP and cyclohexanone) in a manner similar to that described in Example 28 to form ARCs with weight ratios of DCA to other ingredients of 0.60:1.00 and 0.80:1.00. (These values correspond to coated films which contain 37.5 wt. % and 44.4 wt. % dye, assuming the proportions of the ingredients remain the same during the spin coating process.) The two ARCs were spin coated onto round glass slides at 4000 rpm (60 sec) and baked on a hot plate at these respective temperatures: 150°, 168°, 190°, and 210° C. The film thickness (by profilometry) and film absorbance of each specimen were measured shortly after baking. Subsequently, the specimens were placed back on the spin coater and liquid PGMEA was puddled on the coating for five seconds in a static condition and then spun until dry. Film absorbance was then redetermined. (The absorbance loss of the ARC resulting from PGMEA application can be correlated with absorbance loss during the application of a photoresist, a process commonly known as stripping.) The initial film thickness and absorbance data before and after PGMEA application are presented in Table II.

                  TABLE II                                                         ______________________________________                                         Film Thickness and Film Absorbance for Dicinnamalacetone-Loaded                Polyamic Acid-Based ARC as a Function of Bake Temperature and                  Before and After PGMEA Application                                             Calculated                                                                              Bake      Film                                                        Wt. % DCA                                                                               Temperature                                                                              Thickness Film Absorbance at 365 nm                         in ARC film                                                                             (°C.)                                                                             (Å)   Before                                                                               After % Loss                                ______________________________________                                         37.5     150       1327      0.7543                                                                               0.4885                                                                               35.2                                  37.5     168       1215      0.6361                                                                               0.4840                                                                               23.9                                  37.5     190       1013      0.4299                                                                               0.4285                                                                               0.3                                   37.5     210        902      0.2027                                                                               0.2026                                                                               0.0                                   44.4     150       1522      0.9741                                                                               0.4265                                                                               56.2                                  44.4     168       1416      0.8331                                                                               0.5239                                                                               37.1                                  44.4     190       1058      0.5494                                                                               0.5209                                                                               5.2                                   44.4     210        915      0.2095                                                                               0.1976                                                                               5.7                                   Example 28 ARC containing                                                      using 40.1 wt. % Family 3 dye                                                         168     1565      0.7206  0.6845                                                                               5.0                                            200     1545      0.7171  --    --                                             230     1495      0.6799  --    --                                      ______________________________________                                    

The results showed that DCA-loaded ARCs, though highly absorbant at i-line, showed significant sublimative losses as bake temperature increased from 150° C. to 210° C. This was evidenced by a sharp monotonic decrease in starting film absorbance and film thickness as bake temperature was raised. The films were also highly susceptible to stripping by PGMEA (as measuredby % Loss), particularly at the lower bake temperatures. As expected, stripping was more severe for the ARC prepared with a higher dye loading. These results could be contrasted with those (bottom of Table II) for the Example 28 ARC which showed virtually no stripping or sublimative loss at a comparable dye loading.

EXAMPLE 31

Using a sublimable, photoresist-soluble dye in a polyurea-based ARC. Comparison with performance of ARC from Example 29.

An ARC similar to the polyurea composition described in Example 29 was prepared by combining DCA with polyurea in a mixture of THFA and cyclohexanone. The ARC was formulated to provide 28.6 wt. % DCA in the coated film. It was spin coated onto round glass slides at 5500 rpm (60 sec) which were baked on a hot plate at these respective temperatures: 168°, 190°, and 220° C. The film thickness (by profilometry) and film absorbance of each specimen were measured shortly after baking. A PGMEA-based resist (Shipley Microposit® 1470) was spin coated over the ARC and then immediately removed by spraying the specimen with PGMEA for five seconds while spinning. Film absorbance was remeasured to determine the degree of dye stripping resulting from the resist apply and removal process. The initial film thickness and absorbance data before and after resist application are presented in Table III.

                  TABLE III                                                        ______________________________________                                         Film Thickness and Film Absorbance for a Dicinnamalacetone-Loaded              Polyurea-Based ARC as a Function of Bake Temperature and                       Before Resist Application and After Resist Removal                             Calculated                                                                              Bake      Film                                                        Wt. % DCA                                                                               Temperature                                                                              Thickness Film Absorbance at 365 nm                         in ARC film                                                                             (°C.)                                                                             (Å)   Before                                                                               After % Loss                                ______________________________________                                         28.6     168       2180      0.6571                                                                               0.2614                                                                               60.2                                  28.6     190       1980      0.3483                                                                               0.1708                                                                               51.0                                  28.6     220       1800      0.1275                                                                               0.0904                                                                               29.1                                  Example 37 ARC containing                                                      44.4 wt. % Family 1 dye                                                               200     1485      0.5498  0.4259                                                                               22.5                                           220     1460      0.5371  0.4292                                                                               20.1                                    ______________________________________                                    

As in Example 30, the DCA-loaded films showed a sharp drop in absorbance and thickness as bake temperature increased, indicating that dye sublimation was occurring. Likewise, resist application and removal caused a significant reduction in ARC absorbance at all bake temperatures because of the high solubility of DCA in the resist solvent, PGMEA. It should be noted that stripping levels were high even though the DCA content in the as-spun films was low. The Example 29 ARC (see bottom of Table III), on the other hand, exhibited much less stripping than the DCA-loaded ARC at a higher dye loading. The film thickness and absorbance of the Example 29 ARC were also stable at the bake temperatures used in the study. 

What is claimed is:
 1. An improved mid-UV anti-reflective dye of the type useful in ultra-thin sublayers of multi-layer i-line photoresist systems where said sublayer is sandwiched between a top i-line photoresist layer and a microelectronic substrate; the improved dye being characterized as non-subliming and exhibiting differential solubility, said dye being
 1. 4-divinylbenzenes having terminal acetophenones which are substituted at the para (or 4-) ring position or, optionally, substituted in addition at the meta (or 3-) ring position.
 2. The mid-UV-absorbing 1.4-divinylbenzene dyes of claim 1 wherein said dyes have a structural formula of this form, ##STR16## where R₁ is chosen from the group consisting of ##STR17##
 3. The dye of claim 2 corresponding to the following structural formula: ##STR18## 